Powder compression presses for PTFE, ceramic, and metal PM — die design, tonnage selection, and production throughput.
Contact HEMSUN ENGG. INDUSTRIES for expert guidance on PTFE products and hydraulic machinery.
Powder compaction
Dry powder compaction presses form green parts for sintering or further processing. Tonnage, fill height, and ejection are matched to powder type and part geometry.
Material lines
Review metal powder PM presses and ceramic compaction in our compression molding range.
RFQ information
Share powder type, part weight, dimensions, and required production rate for press sizing.
Explore products
Next steps for buyers
When you have reviewed this powder compression machines guide, send your drawing, material grade, and annual quantity to HEMSUN ENGG. INDUSTRIES for a scoped quote from our Dahegam, Gujarat works. Related product and machine pages on hemsun.com list specifications you can link in your RFQ for faster review. Contact info@hemsun.com or sales@hemsun.com with destination port and inspection requirements where applicable.
Buyer checklist
Before you email HEMSUN, confirm drawing revision, material grade, quantity, destination port, and any inspection or certificate requirements for your powder compression machines enquiry so our Dahegam team can respond with accurate lead time and commercial terms.
Technical specifications, testing and engineering data
HEMSUN ENGG. INDUSTRIES manufactures and engineers high-precision solutions for powder compression machines at our Dahegam, Gujarat facility. Operating since 1994, our manufacturing processes combine modern CNC machining centers, precision hydraulic compression presses, and continuous CMM inspection.
Comprehensive Material & Mechanical Property Matrix
| Engineering Property | Virgin PTFE Standard | 25% Glass-Filled PTFE | 33% Carbon-Filled PTFE | 60% Bronze-Filled PTFE | Test Standard |
|---|---|---|---|---|---|
| Specific Gravity | 2.14 – 2.18 g/cm³ | 2.22 – 2.26 g/cm³ | 2.05 – 2.15 g/cm³ | 3.80 – 4.00 g/cm³ | ASTM D792 |
| Tensile Strength | 20 – 35 MPa | 14 – 22 MPa | 12 – 18 MPa | 15 – 24 MPa | ASTM D4894 |
| Elongation at Break | 250% – 450% | 150% – 250% | 80% – 160% | 100% – 200% | ASTM D4894 |
| Compressive Strength (1% strain) | 4.0 – 5.5 MPa | 7.5 – 9.0 MPa | 8.0 – 10.5 MPa | 12.0 – 15.0 MPa | ASTM D695 |
| Deformation Under Load (14 MPa, 24h) | 12% – 15% | 4% – 6% | 3.5% – 5% | 2.5% – 4% | ASTM D621 |
| Shore D Hardness | 50 – 55 Shore D | 58 – 64 Shore D | 60 – 66 Shore D | 65 – 72 Shore D | ASTM D2240 |
| Dynamic Friction Coeff. (vs Steel) | 0.05 – 0.08 | 0.10 – 0.14 | 0.08 – 0.12 | 0.12 – 0.16 | ASTM D1894 |
| Thermal Conductivity | 0.25 W/m·K | 0.40 W/m·K | 0.55 W/m·K | 0.85 W/m·K | ASTM C177 |
Quality Assurance, Testing Protocols & Traceability
- Dimensional CMM Profilometry: Critical diameters, concentricity, and sphericity are verified on coordinate measuring machines against drawing nominals.
- Dielectric Breakdown Voltage Testing: High-voltage spark testing screens moulded parts for micro-voids, pinholes, and internal conductive inclusions before dispatch.
- Specific Gravity & Density Verification: Water displacement density checks according to ASTM D792 ensure full preform compaction and complete oven gel sintering.
- Certificate of Compliance & MTR: Every dispatch includes mill test certificates confirming raw resin lot traceability, filler content, and tensile/elongation values.
Installation, Machining & Maintenance Recommendations
- Tooling Geometry for Machining: Use polished tungsten carbide (C2 grade) or polycrystalline diamond (PCD) inserts with high positive top rake angles (15° to 25°) and sharp cutting edges to prevent material smearing.
- Feed & Speed Rates: High spindle speeds (200 to 450 m/min) combined with moderate feed rates (0.05 to 0.15 mm/rev) ensure mirror surface finishes without localized frictional heating.
- Coolant Application: Water-soluble synthetic coolants or clean air blast prevent thermal expansion during high-speed CNC turning and milling passes.